I purchased my Rolex in Switzerland in the early 1980’s.
It has operated flawlessly all these years …except late 80’s I dropped it on a tile floor and cracked the glass bezel. It was sent to a Rolex repair facility in New York and as I said- worked without issue all these years. I put it in the bank safety deposit box 2 years ago. When I retrieved it recently- I was stunned to notice it was not working. Upon closer inspection I see what appears to be tiny dark pieces (almost like tiny rocks) that roll around the face…also- it appears there is some sort of degradation on the hands and face as well. What on earth is happening here? Does anyone have an idea? Regarding possible repair- I phoned an authorized Rolex dealer/repair facility. They indicate do to the age…they do not offer in house repair…it must be sent to Rolex etc… repair estimate 800-$1300! After I picked myself up off the floor…I found this forum. Hoping someone here has experience in this sort of situation and might guide me towards a reasonable solution. Thank you! (Trying to upload a photo but it’s too large so will try again…) |
![]() |
![]() |
![]() |
#2 |
"TRF" Member
Join Date: Oct 2022
Location: Indiana
Posts: 5
|
![]() |
![]() |
![]() |
![]() |
#3 |
"TRF" Member
Join Date: Jun 2017
Location: Canada
Watch: 1680
Posts: 1,396
|
Possible there was some water intrusion before you locked it away and the moisture just slowly damaged things. Doesn’t sound good. Photos would help.
|
![]() |
![]() |
![]() |
#4 |
TRF Moderator & 2024 SUBMARINER Patron
Join Date: May 2007
Real Name: Larry
Location: Mojave Desert
Watch: GMT's
Posts: 43,370
|
Looks like the lume on your minute hand has deteriorated and is floating around.
The only fix is to take it apart and clean all the old lume out, then either replace the hands or have the original filled with material to match.
__________________
(Chill ... It's just a watch Forum.....) NAWCC Member |
![]() |
![]() |
![]() |
#5 |
"TRF" Member
Join Date: Oct 2022
Location: Indiana
Posts: 5
|
Is this sort of degradation to be expected with a watch this age?
Or did moisturizer and or humidity create the problem? Is there such thing as a Rolex repair facility that is dependable but not necessarily "authorized" ? There is NO way I'm going to pay $1000 to repair a watch. Thanks in advance for any input. |
![]() |
![]() |
![]() |
#6 |
2024 Pledge Member
Join Date: Oct 2018
Location: Colorado, USA
Posts: 6,110
|
It looks like you are losing some of the gray finish from the dial. Unfortunately, that does happen sometimes with the colored dials, but it's not inevitable. So I suspect that the storage conditions contributed.
There are certainly watchmakers that will repair/service Rolex watches. If you find one who has a Rolex parts account, they should be able to work on that watch, since it presumably has a cal 3035. Even without a parts account, some watchmakers can find ways to source parts. If you search the forum, you will find that several independent watchmakers are frequently recommended. However, they also charge premium prices IMO, so you may not find that you are saving a large amount. They will, however, follow your instructions regarding preserving vintage parts. Given the degradation of your dial, a Rolex Service Center might require you to replace the dial and hands with modern parts. You may also want to contact the Rolex Service Center directly. It sounds to me that your AD is planning to add their own fee for sending the watch to the RSC for you. It's actually much better to send the watch to Dallas directly. The communication is better, and you will avoid the middleman.
__________________
@oldwatchdan on IG |
![]() |
![]() |
![]() |
#7 |
"TRF" Member
Join Date: Oct 2022
Location: Indiana
Posts: 5
|
![]()
Holy Cow! Thanks Dan. All good info. Will definitely investigate dealing with Rolex direct...and/or a reputable watch repair outfit. Many thanks!
|
![]() |
![]() |
![]() |
#8 |
2024 ROLEX SUBMARINER 41 Pledge Member
Join Date: May 2008
Real Name: Matt
Location: Wine Country, Ca
Posts: 5,925
|
Keep in mind that safety deposit boxes are not sealed and are still prone to moisture, humidity, dryness, etc.
__________________
TRF Member 11738 |
![]() |
![]() |
![]() |
#9 | |
TRF Moderator & 2024 SUBMARINER Patron
Join Date: May 2007
Real Name: Larry
Location: Mojave Desert
Watch: GMT's
Posts: 43,370
|
Quote:
It appears to be the seconds hand, not the minute hand, that is showing deterioration of the finish. The -TSwissT- markings on the dial indicate steel hands and indices, and they are often plated. It is likely that the plating is breaking up. Most shops can take your watch apart and clean things or replace corroded parts. However, it is unlikely that you will find any who will not clean the entire movement because pieces of this detritis will be inside and affect it's function. A basic service call at Rolex is around 700 bucks, although other shops may be a bit less, they may not be as capable.
__________________
(Chill ... It's just a watch Forum.....) NAWCC Member |
|
![]() |
![]() |
![]() |
#10 |
TRF Moderator & 2024 SUBMARINER Patron
Join Date: Jul 2013
Real Name: Adam
Location: Far East
Watch: SEIKO TUNA
Posts: 28,578
|
Rolex will likely insist on hands and dial replacement if they are degrading to the extent that bits will possibly be falling through the date window and into the movement during the one-year warranty period. In that case the total quote will be quite a bit more than $1k.
__________________
_______________________ |
![]() |
![]() |
![]() |
#11 |
"TRF" Member
Join Date: Oct 2022
Location: Indiana
Posts: 5
|
![]()
It never occurred to me that the bank box would cause such havoc.
I’ve learned a very expensive lesson. It was flawless when placed in the box. Should have just taken it on my 2 year trip. |
![]() |
![]() |
![]() |
#12 |
"TRF" Member
Join Date: Dec 2007
Location: Northumberland,UK
Watch: 1675 GMT
Posts: 640
|
It always amazes me how a Rolex Oyster watch, presumably with the crown screwed down, can be vulnerable to atmospheric humidity in a safe deposit vault. Even if the seals are old, it should still have a good degree of vapour resistance. My 1675 GMT has been subject to normal atmospheric moisture in the north of England for decades yet hasn't suffered any deterioration of this sort.
Learning from other's experience, I reckon that if I was ever to store my watch for an extended period I would seal it in a polythene bag with a desiccant sachet. Stan. |
![]() |
![]() |
![]() |
#13 | |
"TRF" Member
Join Date: Sep 2012
Location: Japan
Posts: 4,361
|
Quote:
The fact is that everything falls apart in the long run. Including us. ![]() |
|
![]() |
![]() |
![]() |